Table of contents

From 0,25 to 1,5 mm

Technical characteristics of stamped parts: Dark grey, density 1.0; temperature + 120 °C, peak temperature + 150 °C, max. pressure 10 bar, compressibility 22.5 %, tensile strength 15 N / mm², very good resistance to oil and fuel, good resistance to acids and alkalis.

From 1,0 to 10,0 mm

Technical characteristics of stamped parts: 60 ± 5 Sh. A, black, density 1.11; temp. range - 40 to + 100 °C, tensile strength 13 MPa, tensile elongation 600 %, good resistance to acids, alkalis and ozone.

From 0,5 to 5 mm

Technical characteristics of stamped parts: Red, density 1.80; temp. range - 200 to + 180 °C, max. pressure 40 bar, good oil resistance, resistance to acids and alkalis conditional, KTW approved (plastic and rubber for drinking water).

From 2,0 to 60,0 mm

Technical characteristics of stamped parts: Cellular epoxy rubber black, 45 ± 10 Sh., density 175 kg / m³; temp. range - 50 to + 95°C, peak temperature +100°C, resistance to alkalis, acids and oil conditional, very good ozone resistance, closed pores, FMVSS 302, SAE J 18- 79, ASTM D 1056-77, AFNOR, NF - R 99-211-80, DBL 5574.10.

From 1,0 to 20,0 mm

Technical characteristics of stamped parts: 60 ± 5 Sh. A, black, smooth on both sides, density 1.06; temperature range : - 35 to + 100 °C, tensile strength 18 MPa, tensile elongation 400 %, very good resistance to alkalis and the ozone, low in nitrosamine, approved according to DIN 4807.

From 1,0 to 20,0 mm

Technical characteristics of stamped parts: 60 ± 5 Sh. A, black, density 1.30; temperature range: - 40 to + 100 °C, tensile strength 5 MPa, tensile elongation 300 %, resistance to acids and alkalis conditional, also available with 1 or 2 duck layers.

From 0,5 to 10,0 mm

Technical characteristics of stamped parts: 50 ± 5 Sh. A, black, KTW, density 1.08; temperature range: - 40 to + 150 °C, tensile strength 12 MPa, tensile elongation 350 %, very good resistance to acids, alkalis and the ozone, meets VW 2.8.1. G50 standard and DBL 5571.20 standard (Daimler-Benz delivery rules), sulphur-free.

From 0,3 to 3 mm

Technical characteristics of stamped parts Fibre: Red, hard, density 1.35; temperature + 95 °C, very good resistance to oil and fuel, resistance to alkalis and acids conditional, KTW (plastic and rubber for drinking water). Also available in grey or black.

From 1,0 to 6,0 mm

Technical characteristics of stamped parts: Red - brown PU, density 0.77; temperature + 110 °C, good resistance to oil, fuel, acids, alkalis, ozone and weather conditions.

From 1,0 to 10,0 mm

Technical characteristics of stamped parts: No duck layer, 45 ± 5 Sh. A, white, density 1.27; temp. range - 30 to + 70 °C, tensile strength 12 MPa, tensile elongation 550 %, food grade, good resistance to alkalis, resistance to acids conditional, BGVV XXI (BGA) Cat. 1 FDA CFR 177.2600.

From 1,0 to 10,0 mm

Technical characteristics of stamped parts: 50 ± 5 Sh., density 1.24; temp. range - 30 to + 90 °C, tensile strength 7 MPa, tensile elongation 500 %, food grade, resistance to acids and alkalis conditional.

From 0,5 to 50,0 mm

Technical characteristics of stamped parts: 70 ± 10 Sh. A, black, density 1.45; temp. range - 30 to + 70 °C, tensile strength 4 MPa, tensile elongation 150 %, resistance to acids and alkalis conditional. Also available with 1 or 2 duck layers.

From 1,0 to 10,0 mm

Technical characteristics of stamped parts: 80 ± 5 Sh. A, black, density 1.35; temp. range - 15 to + 80 °C, short-term peak temperature 110 °C, tensile strength 13 MPa, tensile elongation 250 %, DVR (compression set) 168 h / 100 °C / 35 %, good resistance to acids, alkalis, fuel and oil, ozone resistance conditional, DVGW approved according to standards DIN 3535 1 and 2 and DIN EN 549.

From 0,2 to 5,0 mm

Technical characteristics of stamped parts Hard PVC: White, density 1.45; temp. range - 15 to + 60 °C, volume resistivity 10^{3</supohm.cm, good resistance to acids, oil, fuel and alkalis, low fl ammability, according to DIN 4102 B1, self-extinguishing. Light transparent, light grey or black and red also available.}

From 0,5 to 5 mm

Technical characteristics of stamped parts: Green, density 1.90; max. temp. + 220 °C, max. pressure 80 bar, good resistance to oil and fuel, resistance to alkalis and acids conditional, KTW (plastic and rubber for drinking water), DVGW (German water and gas specialists association).

From 0,01 to 0,35 mm

Technical characteristics of stamped parts: Transparent, density 1.40; temp. range - 19O to + 130 °C, tensile strength 200 MPa, good resistance to oil, fuel, acids and alkalis. Modulus of elasticity 4500 N / mm², tensile elongation 100 %, melting point 260 °C

From 0,3 to 5,0 mm

Technical characteristics of stamped parts: Green, printed, density 1.6O; max. temp. + 400 °C, max. pressure 60 bar, good resistance to oil, alkalis, fuel and acids, HTB (gas and heating test bed), KTW (plastic and rubber for drinking water), WRC (water research centre), BAM, DVGW.

From 0,1 to 6 mm

Technical characteristics of stamped parts LD - PE: Natural, density 0.92; temp. range - 40 to + 60 °C, very good resistance to acids and alkalis, good resistance to oil and fuel, dielectric strength 75 Kv / mm, volume resistivity 10¹⁷², thermal conductibility 0.40 W / mxK, combustibility as per standard DIN 4102 B2.

From 1,0 to 10,0 mm

Technical characteristics of stamped parts: 60 ± 5 Sh. A, light, density 1.46; temp. range - 20 to + 90 °C, tensile strength 6 MPa, tensile elongation 550 %, resistance to acids, alkalis and oil conditional, physiologically inert.

From 1,0 to 15,0 mm

Technical characteristics of stamped parts: 80 ± 5 Sh. A, black, density 1.50; temp. range - 20 to + 70 °C, tensile strength 5 MPa, tensile elongation 200 %, resistance to ozone, oil, alkalis and acids conditional.

From 1,5 to 10,0 mm

Technical characteristics of stamped parts: Light, density 0.90; temperature + 1200 °C, tensile strength 3 MPa, good resistance to oil, fuel, acids and alkalis, loss on ignition 20 % max., other grade available on request.

From 1,0 to 20,0 mm

Technical characteristics of stamped parts: 50 ± 5 Sh. A, black, density 1.30; temp. range - 10 to +70 °C, short-term peak temperature 80 °C, tensile strength 4 MPa, tensile elongation 350 %, DVR (compression set) 22 h / 70 °C / 40 %, resistance to acids and alkalis conditional, good oil resistance.

From 0,5 to 40,0 mm

Technical characteristics of stamped parts: 65 ± 5 Sh. A, black, density 1.35; temp. range - 20 to + 70 °C, tensile strength 5 MPa, tensile elongation 200 %, DVR (compression set) 22 h / 70 °C / 40 %, good oil resistance, resistance to fuel, acids and alkalis conditional. Also available with 1 or 2 duck layers.

From 0,8 to 10,0 mm

Technical characteristics of stamped parts: 65 ± 5 Sh. A, black, density 1.37; temp. range - 20 to + 120 °C, tensile strength 7 MPa, tensile elongation 320 %, resistance to acids, alkalis and ozone conditional, very good resistance to oil and fuel.

From 0,3 to 6,0 mm

Technical characteristics of stamped parts Polystyrol: White, black, density 1.05; max. temp. + 70 °C, good resistance to acids and alkalis, oil resistance conditional, volume resistivity 10^{16</supohm.cm, excellent resistance to cold temperatures, good mechanical properties.}

From 0,05 to 40,0 mm

Technical characteristics of stamped parts PTFE (Teflon): White, pure, density 2.18; temp. range - 200 to + 260 °C, volume resistivity 10^{18</supohm.cm, very good resistance to acids, alkalis, fuel and oil, nonfl ammable, UL 94 VO fi re classifi cation. Also available coated on one side or with glass fibre, charcoal or graphite.}

From 0,5 to 10,0 mm

Technical characteristics of stamped parts: 60 ± 5 Sh. A, red, density 1.17; temp. range - 60 to + 230 °C, tensile strength 5 MPa, tensile elongation 250 %, good resistance to acids, alkalis and ozone, resistance to oil and fuel conditional, food grade, BGA XV- Silicone, FDA # 117.2600.

From 0,1 to 10,0 mm

Technical characteristics of stamped parts soft PVC 70: 67 ± 5 Sh. A, natural, density 1.34; temp. range - 35 to + 50 °C, tensile elongation 260 %, resistance to acids conditional, good resistance to alkalis and oil, volume resistivity 10^{15</supohm x cm.}

From 0,3 to 5 mm

Technical characteristics of stamped parts: Blue, density 1.80; temperature + 250 °C, pressure 100 bar, good resistance to oil and fuel, resistance to acids and alkalis conditional, KTW (plastic and rubber for drinking water), DVGW (German water and gas specialists association), WRC (water research centre). Also available with graphite on both sides.

From 0,5 to 12,0 mm

Technical characteristics of stamped parts: 75 ± 5 Sh. A, black, density 2.0; temp. range - 10 to + 275 °C, tensile strength 9 MPa, tensile elongation 200 %, DVR (compression set) 22 h / 200 °C / 45 %, good resistance to acids, alkalis, fuel, oil and ozone, sulphur-free, self-extinguishing, biphenol, electric insulation.